P 1221 - Design method for cyclically stressed steel/CFRP bonded joints with special consideration of crack propagation

P 1222 - Hot cutting of carbon-martensitic chromium steels in multi-stage processes The use of hot cutting for the production of structural components made of carbon-martensitic chromium steels in the automotive industry offers economic advantages over the currently predominant laser cutting. For example, the elimination of downstream laser trimming leads to a considerable reduction in process time and contributes to an increase in productivity. With hot cutting, no material deposits occur on the surface as a result of spatter and there is potential for savings in tool costs, as cooling channels close to the surface, as required when processing the heat-treatable steel 22MnB5, are not necessary. Chromium steels are currently hardly used in the production of car body components. One reason for this is the lack of experience with regard to the process parameters for hot cutting. As part of this research project, the influence of the process parameters on the cut surface geometry, dimensional accuracy and expansion capacity was therefore scientifically investigated. The focus was on the change in the individual cut surface parameters as a result of different parameter combinations. In addition, fundamental knowledge was gained about the effect of upstream and downstream forming operations on the quality and static properties of the cut parts. The result of the research is the provision of optimal process parameters and thus an increase in the operational readiness of hot cutting processes for the production of mould-hardened components made of chromium steel. Publication: 2021 Authors: Prof. Dr.-Ing. B.-A. Behrens

P 1226 - Holistic modelling of short-term tempering in the process of inductive surface hardening Induction hardening is an energy-efficient process in which undesirable crack-inducing residual stresses also arise due to process-related thermal gradients between the surface and core areas. These are conventionally countered by tempering in the first tempering stage for up to two hours, which is associated with additional transport and energy costs in the process chain. A resource-saving and environmentally friendly alternative is induction tempering, which takes just a few seconds and can be integrated into a running production line. This allows the existing induction hardening process chain to be made more flexible while maintaining the same product and process quality and at the same time enhancing the ecological value of the process. The empirical determination of the induction tempering parameters involves considerable effort, which is why potential users are reluctant to use this process. A virtual process design can significantly reduce the experimental effort and thus increase the attractiveness of this innovative tempering technology. Existing induction tempering models concentrate on modelling electromagnetic-thermal processes and the resulting material hardness without considering the preceding induction hardening process. As a result, the complex coupled thermal-microstructural aspects are neglected, so that the informative value of the models is severely limited. Based on this problem, a holistic numerical model for induction tempering in the induction hardening and tempering process chain was developed in this research project, with which an efficient determination of optimal tempering parameters is possible with reduced effort and a deeper understanding of the process. The model was implemented as an example in the commercial simulation software ANSYS and validated experimentally. Publication: 2021 Authors: Prof. Dr.-Ing. Nacke, Prof. Dr.-Ing. H. J. Maier

P 1216 - Qualification of shear cutting for making holes in steel structures Pre-hole production by shear cutting makes a significant contribution to increasing productivity. According to DIN EN 1090-2 [1], pre-hole production by shear cutting is only permissible in steel construction if t < 1.4 ? d. In connections subject to cyclic or seismic loads, lap joints with bolts above strength class 8.8 or in slip-resistant connections, shear cutting of the nominal hole diameter is generally not permitted. In DIN EN 1090-2 [1], only limited attention is paid to the hole condition and the production-related boundary conditions for shear cutting. When using shear cutting as a cost-effective pre-punching process, the production parameters such as cutting gap or punch and die geometry have a decisive influence on the cut surface quality and therefore also on the material and load-bearing behaviour in the area of the hole or the related residual cross-section of the component. By adapting the cutting parameters and system technology, it is possible to achieve up to 100 % smooth cut with no burrs. Holes produced in this way in the steel material S235JR achieve better vibration resistance behaviour than the drilled hole for component thicknesses t = 6 mm (DSt = 13 mm) and t = 10 mm (DSt = 9 mm and DSt = 13 mm). A comparison of the punched perforated bars with the drilled perforated bars does not reveal any influence of shear cutting that reduces the vibration resistance. In addition to the steel material S235JR, other steel materials such as S355J2+N, S460MC, S250GD, S350GD and HX420LAD were used in several component thicknesses. Here, too, it can be seen that a defined specification of cutting parameters (reduction of the cutting gap) has significantly improved the result of the fatigue strength test compared to state-of-the-art shear cutting. shear cutting. Publication: 2020 Authors: Prof Füssel, Prof Wanner

P 1227 - Joining of duplex steels by means of laser beam-UP hybrid welding Due to their excellent properties, duplex steels are used for applications in the oil and gas industry and in ship and bridge building that are subject to corrosion. In addition to corrosion resistance, such steels are characterised by high strength and toughness, which is due to a delta ferrite-austenite microstructure ratio of at least 30 % austenite. This microstructure ratio can be lost during welding due to unfavourable heat conduction. Arc welding processes, such as SAW and GMAW, have become established in practice for welding duplex steels. These welding processes can produce joints with the required microstructure ratio, but at the compromise of low productivity. The beam welding processes laser beam welding or electron beam welding, on the other hand, have a high productivity, but cannot produce welded joints with the required microstructure ratio. Laser beam-UP hybrid welding combines the advantages of both welding processes and can be a good alternative with high productivity. The aim of the research project was to be able to produce weld seams on duplex steel 1.4462 (up to 30 mm) with high weld seam quality in terms of mechanical-technological properties and corrosion resistance using laser beam-UP hybrid welding in a reliable and efficient process. As part of the welding process development, welded joints were produced from duplex steel 1.4462 by varying process parameters such as laser beam power, feed rate and oscillation amplitude and evaluated in terms of metallurgical and mechanical properties based on standards and regulations. Cross-sections, EDX analyses, microstructural analyses, notched bar impact bending tests, tensile tests and corrosion tests were used to qualify weld seams. As a key result, efficient high-performance welding processes with a laser beam power of up to PL = 16 kW and a submerged arc power of PUP = 15 kW at a welding speed of up to vS = 1.0 m/min were achieved. The welded joints produced do not exhibit any critical irregularities and for the most part achieve the required austenite content of 30 %, the required impact energy of KV-min = 40 J at a test temperature of -40 °C and corrosion resistance in line with requirements. Based on these results, laser beam-UP hybrid welding has proven to be a reliable welding process with high productivity, which could play an important role in the future for the welding production of components made of duplex steels. Publication date: July 2022 Authors: Dipl.-Ing. M. Puschmann, P. Urbanek, Dr.-Ing. F. Riedel, Prof. Dr.-Ing. St. Kaierle, Dr.-Ing. R. Lahdo, Dr.-Ing. S. Nothdurft, Dr.-Ing. J. Hermsdorf