P 1248 - Qualification of the instrumented indentation test for the determination of characteristic values for high-strength steels with welds

P 1247 - Development of incremental microforming for the production of functional samples of metallic bipolar plates The aim of the research project was the production of functional samples of metallic bipolar plates by means of incremental forming. The development of the tool technology, the derivation of process control strategies and the testing of the application behaviour of the manufactured components formed the focal points of the work programme. The evaluation of bipolar plate designs in the context of fuel cell development was primarily carried out through experimental testing. Despite the small quantities (1 10 pieces) of prototypes required, these have so far been produced by deep drawing or hydroforming. The cost of the tools required for this represents a significant obstacle to innovation in the development process. By manufacturing metallic bipolar plates using incremental forming, the costs of the prototyping process should be significantly reduced. This was to be made possible by the reduced die load, which enables the use of cost-effective tool concepts. The challenge in achieving this goal was the development of graver tools for moulding the delicate channel structures. The thickness of the steel foils to be moulded of s0 = 0.1 mm also requires a friction-reducing tool design. In addition to assessing the geometric accuracy, the manufactured components were also tested with regard to their operating behaviour as a bipolar plate for a fuel cell. The reduced financial risk and the shorter development cycles in the production of functional prototypes using incremental moulding represent a significant competitive advantage. The machine tools required for the production of patrices and for forming are often also available to SMEs with limited machinery. This enables the development of new business areas without new investments. Small companies can thus establish themselves as manufacturers of patrices and tools and as service providers in the field of forming. Publication: 2019 Authors: Prof. Dr.-Ing. Dr.-Ing. E.h. A. E. Tekkaya, Prof. Dr. A. Heinzel

P 1249 - Increasing the wear resistance of forging tools by using an intelligent hot-work tool steel in combination with a material-specific nitriding treatment Forging tools made of an intelligent hot-work tool steel developed by alloying have good wear resistance in thermomechanically highly stressed tool areas. This is due to an alloy-specific mechanism of cyclic surface layer hardening, which ensures continuous protection of these wear-prone areas. However, due to the varying stresses in the different tool areas, the increased wear resistance is locally limited. The aim of the current research project was to increase the wear resistance of forging tools by using this intelligent hot-work tool steel in combination with a material-specific nitriding treatment. In order to realise global wear protection, forging tools made of an intelligent hot-work tool steel were subjected to a surface layer treatment by nitriding, so that an increase in wear resistance was ensured in areas subject to low thermomechanical stress. In addition to characterising the transformation and material behaviour, the main focus of the research project was on developing a nitriding treatment adapted to the intelligent hot-work tool steel and determining the performance of the surface layer-treated forging tools in model tests and industrial practice. Cyclic re-hardening of the tool surface layer was demonstrated in series forging tests after removal of the nitriding zone. Areas subject to insufficient thermomechanical stress were protected from wear by the nitriding zone. In an industrial environment, the nitrided tools made from the modified hot-work tool steel predominantly achieved tool life comparable to the reference condition. Crack formation in the tool contour was considered to be the main cause of failure. The results obtained contribute to the efficient utilisation of the mechanism of cyclic surface hardening in combination with a nitriding zone. Small and medium-sized steel production and processing companies gain a new knowledge base for the development of innovative materials and tools adapted to forming technology processes, gain the opportunity to place new products on the market and benefit from the results in the form of an effective wear protection measure to increase the tool life of hot forging tools. Publication: 2021 Authors: Prof. Dr.-Ing. B.-A. Behrens, Prof. Dr.-Ing. H. J. Maier

P 1243 - Method development for long-term prediction of bonded joints under combined temperature and media exposure The prediction of the ageing behaviour of adhesives is one of the major unresolved issues in adhesive bonding technology. Understanding the long-term behaviour under hygrothermo-mechanical stresses is an essential step towards confidence in adhesive bonding technology and thus to its increased use. However, most approaches to describing the effects of the state of the art only provide a rough estimate of the service life. The water absorption of the adhesive is analysed by means of gravimetric tests. This results in the diffusion rate and the saturation mass as a function of temperature and relative humidity. The water sorption of the adhesive layer is modelled using the FICK diffusion model. The influences of humidity and temperature on the saturation state are taken into account. The dependence of the diffusion coefficient on temperature is modelled using an ARRHENIUS-type approach. The influence of combined hygro-thermo-mechanical (htm) stress on the short and long-term behaviour of the bonded joints is investigated using perforated head tension and thick tensile shear specimens. Firstly, the quasi-static strength of the bonded joint is tested under different constant htm loads. The influence of moisture and temperature on the creep rupture strength is then systematically analysed using creep tests under different climatic conditions. The adhesive layer is modelled with an adhesive layer replacement model, which consists of a rheological model with damage. The rheological model describes the linear viscoelastic behaviour and the damage model describes the failure due to htm stress. The influences of temperature and moisture on the viscoelasticity are recorded with the time-temperature-water concentration shift. Multiaxiality during failure is taken into account by defining an equivalent stress. The concept developed for the long-term prediction of structural bonded joints is applied to the sheet metal tensile shear specimen as part of a case study. The FE simulation is carried out with LS-DYNA, utilising the analogy of the heat conduction and diffusion problem. The case study shows how the service life is predicted on the basis of the transient FE simulation. The influences of the viscoelastic properties on the failure behaviour and the resulting fracture times are shown. Publication: 2021 Authors: Prof. Dr.-Ing. G. Meschut, Prof. Dr.-Ing. A. Matzenmiller

P 1242 - Local concept for the design of elastic bonded joints As part of this research project, a method for direct high-resolution deformation measurement in bonded joints was developed to support the classification of existing design methods for bonded joints and to open up the possibility of new ones. At the Institute of Joining and Welding Technology at the TU Braunschweig (ifs), the new method based on in-situ computer tomography was used and further developed in such a way that measurements can be carried out on various bonded joints under different mechanical stresses. At the same time, the Laboratory for Materials and Joining Technology at Paderborn University (LWF) carried out the modelling and verification of the measurement method. Tensile tests with gradually increasing loads were carried out in coordination between the participating research institutes on adhesive substance samples and inhomogeneously stressed sample geometries in the form of simply overlapped tensile shear and head tensile samples. In-situ computed tomography measurements and measurements using grey value correlation for selected load levels were carried out after relaxation had ceased. From the detected movements of the particles, three-dimensional displacement fields corresponding to the respective load level could be calculated using a suitable evaluation algorithm. A comparison of the displacements measured on the surface using grey value correlation and the three-dimensional displacement fields calculated from in-situ computer tomography measurements served to verify the generated FE models. As a suitable simulation model, the MARLOW model provided the best matches for the numerical modelling. The parameterisation was carried out using the stress and longitudinal strain values determined from tensile tests as well as the transverse contraction coefficient or, alternatively, the transverse strain curve. The parameter sets and simulation models determined and validated by the research institutes for analysing bonded joints can be used directly by SMEs, such as manufacturers of software for calculating bonded joints. In general, confidence in adhesive bonding technology is strengthened by the in-depth understanding of adhesive behaviour under certain influences and improved design methods through simulation, which strengthens the companies active in this field of technology. Publication: 2021 Authors: Prof. Dr.-Ing. K. Dilger, Prof. Dr.-Ing. G. Meschut